Thermal fracturing in glass occurs when sufficient temperature differential is created within glass.〔Technical note no: 65 ("Centre For Window and Cladding Technology" )〕 As a warmed area expands or a cooled area contracts, stress forces develop potentially leading to fracture. A temperature differential may be created in many ways including solar heating, space heating devices, fire, hot and cold liquids. Sloping glass surfaces are subject to greater solar radiation than vertical surfaces and so are more prone to solar thermal fracture. In framed window glass the edges are relatively cooler than the exposed areas so space heating devices in very close proximity may cause thermal fracture. ==Factors affecting thermal stress== *Solar absorption: the temperature of glass depends on the amount of heat absorbed by the glass. So a high performance solar control glass will absorb more heat. so it will be more prone to thermal fracture *Shadow: the presence of shadows will result in relatively cooler areas in glass. Thus it results in temperature difference and may result in thermal fracture. *Edge strength: crack will form if the tensile strength of glass edge exceeds the critical point. Clean cut glass is the strongest and after that polished edge is strongest. *Artificial heating and cooling: if heating or cooling vents are present, the glass can heat or cool excessively and may result in thermal stress. *Frame type and colour: insulating materials keep the edges cool but conduction materials are influenced by their colour. dark colours are more absorptive so causes more heating. *glass type : edge strength of wired glass is less than of ordinary glasses due to weakening caused by cutting processes.〔Thermal Stress And ThermalFracture ("Viridian Glass" )〕 抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』 ■ウィキペディアで「Thermal fracturing in glass」の詳細全文を読む スポンサード リンク
|